密度 | 1.04g/cm3 | 熔體流動速率 | 2.5g/10min | 吸水率 | 0.3% |
缺口沖擊強(qiáng)度 | 21 | 成型收縮率 | 0.4% |
|
產(chǎn)品簡述
密度 | 1.04g/cm3 | 熔體流動速率 | 2.5g/10min | 吸水率 | 0.3% |
缺口沖擊強(qiáng)度 | 21 | 成型收縮率 | 0.4% |
詳細(xì)數(shù)據(jù)
訂購指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 | 比重 | ASTM D-792 | 1.04 | ||
吸水率 | ASTM D-570 | 0.3 | % | ||
成型收縮率 | ASTM D-955 | 0.3-0.5 | % | ||
機(jī)械性能 | 沖擊強(qiáng)度 | (Notched)1/8" | ASTM D-256 | 21 | kg.cm/cm |
彎曲強(qiáng)度 | ASTM D-790 | 680 | kg/cm2 | ||
流動系數(shù) | 200℃/5kg | ASTM D-1238 | 2.5 | G/10min | |
洛氏硬度 | ASTM D-785 | R-107 | R-Scale | ||
伸長率 | ASTM D-638 | 11 | % | ||
拉伸強(qiáng)度 | ASTM D-638 | 480 | kg/cm2 | ||
彎曲模量 | ASTM D-790 | 26500 | kg/cm2 | ||
熱性能 | 燃燒率 | CSA-0.6 | HB | ||
熱變形溫度 | (Unannealed) | ASTM D-648 | 86 | ℃ | |
燃燒率 | UL-94 | HB | |||
軟化點(diǎn) | ASTM D-1525-82 | 104 | ℃ |