斷裂伸長率 | 120% | 密度 | 1.14g/cm3 | 彎曲強度 | 58.82MPa |
吸水率 | 1.3% | 成型收縮率 | 2.2% | 加工級別 | 注塑級 |
特性級別 | 標準級 |
|
產(chǎn)品簡述
斷裂伸長率 | 120% | 密度 | 1.14g/cm3 | 彎曲強度 | 58.82MPa |
吸水率 | 1.3% | 成型收縮率 | 2.2% | 加工級別 | 注塑級 |
特性級別 | 標準級 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
基本性能 | 吸水率 | ASTM D-570 | 8.8 | % | |
吸水率 | ASTM D-570 | 1.3 | % | ||
成型收縮率 | UBEmethod | 2.2 | % | ||
成型收縮率 | UBEmethod | 1.7 | % | ||
物理性能 | 比重 | ASTM D-792 | 1.14 | ||
機械性能 | 彎曲彈性率 | 23° | ASTM D-790 | 11500 | kgf/cm2 |
彎曲彈性率 | 23° | ASTM D-790 | 29000 | kgf/cm2 | |
彎曲強度 | -30° | ASTM D-790 | 1400 | kgf/cm2 | |
1%變形下的壓縮強度 | 23° | ASTM D-695 | 210 | kgf/cm2 | |
屈服下的伸張強度 | 80° | ASTM D-638 | 400 | kgf/cm2 | |
彎曲彈性率 | 80° | ASTM D-790 | 5000 | kgf/cm2 | |
屈服下的伸張強度 | 23° | ASTM D-638 | 540 | kgf/cm2 | |
彎曲彈性率 | -30° | ASTM D-790 | 42000 | kgf/cm2 | |
彎曲強度 | -30° | ASTM D-790 | 1300 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 120 | ||
屈服下的延伸率 | 23° | ASTM D-638 | 6 | % | |
斷裂下的伸張強度 | 23° | ASTM D-638 | 650 | kgf/cm2 | |
擠剪強度 | 23° | ASTM D-732 | 700 | kgf/cm2 | |
屈服下的伸張強度 | 80° | ASTM D-638 | 430 | kgf/cm2 | |
抗沖擊強度 | 23° | ASTM D-256 | 30 | kgf.cm/cm | |
TABER磨耗率 | ASTM D-1044 | 5 | mg | ||
屈服下的伸張強度 | -30° | ASTM D-638 | 1100 | kgf/cm2 | |
屈服下的伸張強度 | -30° | ASTM D-638 | 1150 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 100 | ||
1%變形下的壓縮強度 | 23° | ASTM D-695 | 110 | kgf/cm2 | |
彎曲彈性率 | 80° | ASTM D-790 | 9000 | kgf/cm2 | |
彎曲強度 | 23° | ASTM D-790 | 1100 | kgf/cm2 | |
擠剪強度 | 23° | ASTM D-732 | 650 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 65 | ||
彎曲強度 | 23° | ASTM D-790 | 600 | kgf/cm2 | |
斷裂下的延伸率 | 23° | ASTM D-638 | 120 | % | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 90 | ||
屈服下的伸張強度 | 23° | ASTM D-638 | 780 | kgf/cm2 | |
抗沖擊強度 | -30° | ASTM D-256 | 3.0 | kgf.cm/cm | |
彎曲彈性率 | -30° | ASTM D-790 | 40000 | kgf/cm2 | |
斷裂下的延伸率 | 23° | ASTM D-638 | >200 | % | |
抗沖擊強度 | 23° | 5.0 | |||
電氣性能 | IEC電路 | UL 746 | 600+ | V | |
介電損耗 | 106HZ | ASTM D-150 | 0.08 | ||
介電損耗 | 103HZ | ASTM D-150 | 0.02 | ||
體積電阻率 | ASTM D-257 | 1015 | Ω.cm | ||
介電損耗 | 60HZ | ASTM D-150 | 0.01 | ||
抗電弧強度 | ASTM D-495 | 182 | S | ||
介電損耗 | 106HZ | ASTM D-150 | 0.02 | ||
介電損耗 | 103HZ | ASTM D-150 | 0.07 | ||
介電常數(shù) | 106HZ | ASTM D-150 | 4.1 | ||
絕緣耐力 | ASTM D-149 | 20 | KV/mm | ||
介電損耗 | 60HZ | ASTM D-150 | 0.07 | ||
體積電阻率 | ASTM D-257 | 1013 | Ω.cm | ||
介電常數(shù) | 60HZ | ASTM D-150 | 3.9 | ||
介電常數(shù) | 60HZ | ASTM D-150 | 7.0 | ||
介電常數(shù) | 103HZ | ASTM D-150 | 6.0 | ||
介電常數(shù) | 103HZ | ASTM D-150 | 3.8 | ||
介電常數(shù) | 106HZ | ASTM D-150 | 3.4 | ||
熱性能 | 熱變形溫度 | 18.6kgf/cm2 | ASTM D-648 | 90 | °C |
燃燒率 | UL 94 | V-2 | |||
熱變形溫度 | 4.6kgf/cm2 | ASTM D-648 | 230 | °C | |
熔點 | DSC | 255-265 | °C | ||
線性熱膨脹系數(shù) | ASTM D-696 | 8 | X的10-5cm/cm/°C |