詳細(xì)數(shù)據(jù)
訂購(gòu)指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 | 比重 | ASTM D792 | 1.12 | g/cm3 | |
流動(dòng)熔流率 | 190℃/2.16kg | ASTM D1238 | 10 | g/10min | |
流動(dòng)收縮率 | 2.00mm | ASTM D955 | 0.50 | % | |
平衡吸水率 | 23℃,65%RH | ASTM D570 | 0.48 | % | |
硬度計(jì)硬度 | 支撐 A | JIS K6301 | 89 | ||
硬度計(jì)硬度 | 支撐 D | ASTM D2240 | 38 | ||
機(jī)械性能 | 抗張強(qiáng)度 | ASTM D638 | 23.0 | MPa | |
50%應(yīng)變 | ASTM D638 | 6.40 | MPa | ||
斷裂伸長(zhǎng)率 | ASTM D638 | 690 | % | ||
彎曲模量 | ASTM D790 | 51.0 | MPa | ||
壓縮強(qiáng)度 | 10%應(yīng)變 | ASTM D695 | 4.60 | MPa | |
抗泰伯磨耗 | 1000 Cycles | ASTM D1044 | 20.0 | mg | |
撕裂強(qiáng)度 | ASTM D624 | 98.0 | kN/m | ||
壓縮永久變形 | ASTM D395 | 50 | % | ||
懸壁梁缺口沖擊強(qiáng)度 | ASTM D256 | 無(wú)斷裂 | |||
熱性能 | 熱變形溫度 | 1.8MPa,未退火 | ASTM D648 | <25.0 | ℃ |
脆化溫度 | ASTM D746 | <-65.0 | ℃ | ||
維卡軟化溫度 | ASTM D1525 | 120 | ℃ | ||
熔融溫度 | DSC | 172 | ℃ | ||
流動(dòng)線形膨脹系數(shù) | ASTM D696 | 0.00017 | ℃ | ||
UL 阻燃等級(jí) | UL 94 | HB | |||
電氣性能 | 體積電阻率 | ASTM D257 | 2.0E+12 | ohm.cm | |
介電強(qiáng)度 | ASTM D149 | 20 | kV/mm |