性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 |
比重 | ASTM D792 | 0.992 |
g/cm3;
|
|
熔流率 | 235°C/1.0 kg | ASTM D1238 | 5.0 |
g/10 min
|
|
收縮率 |
流動: 3.18 mm
|
ASTM D955 | 0.80 | % | |
橫向流動: 3.18 mm
|
ASTM D955 | 0.60 | % | ||
硬度計硬度 | 支撐 A | ASTM D2240 | 48 | ||
支撐 A, 10 秒
|
ASTM D2240 |
45 到 55
|
|||
機械性能 |
抗泰伯磨耗 | 1000 Cycles, 1000 g, H-22 轉(zhuǎn)輪 | ASTM D3389 | 58.9 |
mg
|
剝離強度 | 90° | ASTM D429 | 3.6 |
kN/m
|
|
拉伸永久變形 | 100% 應(yīng)變 | ASTM D412 | 4 | % | |
拉伸應(yīng)力 |
50%應(yīng)變
|
ASTM D412 | 1.50 |
MPa
|
|
100%應(yīng)變
|
ASTM D412 | 1.99 |
MPa
|
||
300%應(yīng)變
|
ASTM D412 | 3.36 |
MPa
|
||
抗張強度 | 屈服 | ASTM D412 | 11.3 |
MPa
|
|
伸長率 | 斷裂 | ASTM D412 | 870 | % | |
撕裂強度 | ASTM D624 | 52.2 |
kN/m
|
||
壓縮永久變形 | 23°C, 22.0 hr | ASTM D395B | 22 | % | |
70°C, 22.0 hr | ASTM D395B | 73 |
%
|
||
100°C, 22.0 hr
|
ASTM D395B | 89 |
%
|
||
落錘沖擊 | -30°C | ASTM D5420 | 27.0 |
J
|