斷裂伸長率 | 617% | 拉伸強度 | 37.142MPa | 熔體流動速率 | 3.5g/10min |
用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 | 彎曲模量 | 627.2MPa |
|
產(chǎn)品簡述
斷裂伸長率 | 617% | 拉伸強度 | 37.142MPa | 熔體流動速率 | 3.5g/10min |
用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 | 彎曲模量 | 627.2MPa |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
其它性能 | Elmendorf Tear Strength | ASTM D-1922 | 1.65/3.02(MD/TD) | (g/jη) | |
基本性能 | 熔體流動速率 | ASTM D-1238 | 3.5 | g/10min | |
機械性能 | 1%彎曲模量 | ASTM D-882 | 6400(MD) | kg/cm2 | |
伸長率 | ASTM D-638 | 645/617(MD/TD) | % | ||
拉伸斷裂強度 | ASTM D-638 | 504/379(MD/TD) | kg/cm2 | ||
拉抻屈服強度 | ASTM D-638 | 214/194(MD/TD) | kg/cm2 | ||
其它性能 | 霧度 | ASTM D-1003 | 12 | % | |
Falling Dart Inpact Strength | ASTM D-1709 | 445 | (g) | ||
魚眼 | SK Method | 5 | (ea./600P) | ||
滑動劑 | SK Method | NB | |||
薄膜厚度 | SK Method | 45 | µm | ||
防結(jié)塊劑 | SK Method | NB |