性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
物理性能 | 吸收率 | 23℃,60%RH | ASTM D-570 | 0.22 | % | |
比重 | ASTM D-792 | 1.41 | ||||
機(jī)械性能 | 伸縮率 | 23℃ | ASTM D-638 | 55 | % | |
斷裂強(qiáng)度 | t2mm | ASTM D-732 | 560 | kgf.cm/cm2 | ||
洛氏硬度 | ASTM D-785 | M80 | M scale | |||
曲折彈性率 | 23℃ | ASTM D-790 | 2.65 | ×104kgf/cm2 | ||
彎曲強(qiáng)度 | 23℃ | ASTM D-790 | 920 | kgf.cm/cm2 | ||
120D沖擊強(qiáng)度 | Notch t3.2mm | ASTM D-256 | 6.0 | kgf.cm/cm | ||
拉伸強(qiáng)度 | 23℃ | ASTM D-638 | 620 | kgf.cm/cm2 | ||
拉伸沖擊強(qiáng)度 | t3.2mm S type | ASTM D-1822 | 110 | kgf.cm/cm2 | ||
電氣性能 | 耐電壓 | ASTM D-149 | 19 | KV/mm | ||
表面電阻率 | ASTM D-257 | 1×1016 | Ω | |||
導(dǎo)電率 | 106HZ | ASTM D-150 | 3.7 | |||
體積電阻率 | ASTM D-257 | 1×1014 | Ω.cm | |||
個(gè)質(zhì)損耗系數(shù) | 106HZ | ASTM D-150 | 0.007 | |||
熱性能 | 燃燒性 | t0.8mm | UL 94 | HB | ||
熔體流動(dòng)速率 | ASTM D-1238 | 16 | g/10min | |||
熱變形溫度 | 4.6kgf/cm2 | ASTM D-648 | 158 | ℃ | ||
18.6kgf/cm2 | ASTM D-648 | 110 | ℃ | |||
線膨脹系數(shù) | 20℃-80℃ | ASTM D-696 | 13 | ×10-5cm/cm/℃ | ||
熔點(diǎn) | 10℃/min | DSC Method | 165 | ℃ | ||
其它性能 | 成型收縮率 | t3mm,直徑100mm | 2.0 | % |