密度 | 1.17g/cm3 | 熔體流動速率 | 3.6g/10min | 吸水率 | 0.4% |
缺口沖擊強度 | 2 | 成型收縮率 | 0.5% |
|
產(chǎn)品簡述
密度 | 1.17g/cm3 | 熔體流動速率 | 3.6g/10min | 吸水率 | 0.4% |
缺口沖擊強度 | 2 | 成型收縮率 | 0.5% |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
基本性能 | 熔體流動速率 | 230°C.3.8kg | ASTM D-1238 | 3.6 | g/10min |
吸水率 | 24hr | ASTM D-570 | 0.4 | % | |
物理性能 | 折射率 | ASTM D-542 | 1.49 | nd | |
比重 | ASTM D-792 | 1.17 | |||
全光線透射系數(shù) | 3.2mm | ASTM D-1003 | 92 | % | |
機械性能 | 延展率 | ASTM NO.1 | ASTM D-638 | 80 | % |
成形收縮率 | ASTM D-955 | 0.3-0.7 | % | ||
抗彎強度 | 1/4"棒 | ASTM D-790 | 800 | Kg/cm2 | |
彎曲彈性模量 | 1/4"棒 | ASTM D-790 | 2.3×104 | Kg/cm2 | |
洛氏硬度 | ASTM D-785 | 65 | M scale | ||
懸臂梁式?jīng)_擊強度 | 1/4"付 | ASTM D-256 | 2 | kg.cm/cm | |
抗拉強度 | ASTM NO.1 | ASTM D-638 | 520 | Kg/cm2 | |
電氣性能 | 介質(zhì)損耗角正切 | 60HZ | JIS K-6911 | 0.04 | |
絕緣擊穿強度 | JIS K-6911 | 18 | kv/mm | ||
體積電阻系數(shù) | JIS K-6911 | >1×1015 | Ω.m | ||
介電常數(shù) | 60HZ | JIS K-6911 | 3.8 | ||
表面電阻系數(shù) | JIS K-6911 | >1×1016 | Ω | ||
耐電弧性 | JIS K-6911 | 沒有痕跡 | |||
熱性能 | 載荷撓曲溫度 | 18.56kg/cm2 | ASTM D-648 | 86 | °C |
熱傳導系數(shù) | ASTM D-177 | 5×10-4 | cal/s/cm/°C | ||
維卡軟化溫度 | 1kg | ASTM D-1525 | 101 | °C | |
線膨脹系數(shù) | ASTM D-696 | 8×10-5 | cm/cm/°C | ||
比熱 | C 0.35 | cal/g/°C |