性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 |
密度
|
ASTM D1505 |
1.24
|
g/cm3;
|
|
機械性能 | 薄膜厚度 | 經(jīng)測試 | 25 |
µm
|
|
割線模量
|
MD: 25 µm
|
ASTM D882 | 3310 |
MPa
|
|
TD: 25 µm
|
ASTM D882 | 3860 |
MPa
|
||
抗張強度
|
MD: 屈服, 25 µm
|
ASTM D882 | 110 |
MPa
|
|
TD: 屈服, 25 µm
|
ASTM D882 | 145 |
MPa
|
||
MD: 斷裂, 25 µm
|
ASTM D882 | 110 |
MPa
|
||
伸長率
|
MD: 斷裂, 25 µm
|
ASTM D882 | 160 | % | |
TD: 斷裂, 25 µm
|
ASTM D882 | 100 | % | ||
埃爾曼多夫抗撕強度
|
MD: 25 µm
|
ASTM D1922 | 15 |
g
|
|
TD: 25 µm
|
ASTM D1922 | 13 |
g
|
||
透氧率
|
ASTM D3985 | 220 |
cm3;·mm/m2;/atm/24 hr
|
||
水氣透過率
|
ASTM F1249 | 130 |
g·mm/m2;/atm/24 hr
|
||
Spencer Impact
|
2.50 |
J
|
|||
二氧化碳傳輸速率
|
ASTM D1434 | 76 |
cm3;·mm/m2;/atm/24 hr
|
||
熱性能 |
熔融溫度
|
135 | ℃ | ||
光學性能 | 光澤度 | 20℃ | ASTM D2457 | 90 | |
霧度 | ASTM D1003 | 2.1 | % |