拉伸強(qiáng)度 | 117.6MPa | 密度 | 1.54g/cm3 | 吸水率 | 0.06% |
缺口沖擊強(qiáng)度 | 7 | 成型收縮率 | 7.5% |
|
產(chǎn)品簡述
拉伸強(qiáng)度 | 117.6MPa | 密度 | 1.54g/cm3 | 吸水率 | 0.06% |
缺口沖擊強(qiáng)度 | 7 | 成型收縮率 | 7.5% |
詳細(xì)數(shù)據(jù)
訂購指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
物理性能 | 吸水率 | ASTM D-570 | 0.06 | % | ||
伸長率 | ASTM D-638 | 3.0 | % | |||
模塑收縮率 | 6-9 | |||||
比重 | ASTM D-792 | 1.54 | ||||
機(jī)械性能 | 磨擦系數(shù) | ASTM D-1984 | 0.2 | |||
彎曲強(qiáng)度 | ASTM D-790 | 1800 | kg/cm2 | |||
沖擊強(qiáng)度 | 缺口 | ASTM D-256 | 7.0 | kg.cm/cm | ||
無缺口 | ASTM D-256 | 60 | kg.cm/cm | |||
拉伸強(qiáng)度 | ASTM D-638 | 1200 | kg/cm2 | |||
洛氏硬度 | ASTM D-785 | 90 | M(R) | |||
彎曲模量 | ASTM D-790 | 80000 | kg/cm2 | |||
電氣性能 | 介電定數(shù) | 106Hz | ASTM D-150 | 3.6 | ||
抗弧性 | ASTM D-495 | 80 | Sec | |||
介電定數(shù) | 100Hz | ASTM D-150 | 3.8 | |||
介電強(qiáng)度 | ASTM D-149 | 24 | KV/mm | |||
誘電正接 | 100Hz | ASTM D-150 | 0.002 | |||
抗體積性 | ASTM D-257 | >1016 | Ω.cm | |||
誘電正接 | 106Hz | ASTM D-150 | 0.02 | |||
熱性能 | 線性膨脹系數(shù) | ASTM D-696 | 3×0.000005 | mm/mm/℃ | ||
阻燃性 | HB | |||||
熱變形溫度 | 18.6kg/cm2 | ASTM D-648 | 195 | ℃ | ||
熱變形溫度 | 18.6kg/cm2 | ASTM D-648 | 215 | ℃ |