斷裂伸長率 | 300% | 密度 | 1.31g/cm3 | 吸水率 | 0.08% |
彎曲模量 | 2340MPa | 缺口沖擊強度 | 53.4 | 加工級別 | 注塑級 |
|
產(chǎn)品簡述
斷裂伸長率 | 300% | 密度 | 1.31g/cm3 | 吸水率 | 0.08% |
彎曲模量 | 2340MPa | 缺口沖擊強度 | 53.4 | 加工級別 | 注塑級 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
物理性能 | 密度 | ASTM D792 | 1.31 | g/cm3 | ||
吸水率 | ASTM D570 | 0.08 | % | |||
機械性能 | 屈服拉伸強度 | ASTM D638 | 51.7 | Mpa | ||
斷裂拉伸強度 | ASTM D638 | 51.7 | Mpa | |||
斷裂伸長率 | ASTM D638 | 300 | % | |||
彎曲模量 | ASTM D790 | 2340 | Mpa | |||
屈服彎曲強度 | ASTM D790 | 82.7 | Mpa | |||
斷裂彎曲強度 | ASTM D790 | 82.7 | Mpa | |||
Izod缺口沖擊強度 | ASTM D256 | 53.4 | J/m | |||
Izod無缺口沖擊強度 | ASTM D4812 | 1600 | J/m | |||
洛氏硬度 | ASTM D785 | 117 | R | |||
電氣性能 | 體積電阻率 | ASTM D257 | >4.0E+16 | Ohm.cm | ||
介電強度 | 1.6mm | ASTM D149 | 23 | KV/mm | ||
介電常數(shù) | 100Hz | ASTM D150 | 3.3 | |||
介電損耗 | 100Hz | ASTM D150 | 0.002 | |||
熱性能 | 熱變形溫度 | - | 1.8Mpa | ASTM D648 | 54.4 | ℃ |
- | 0.45Mpa | ASTM D648 | 154 | ℃ | ||
阻燃性 | UL94 | HB |