斷裂伸長率 | 200% | 密度 | 1.14g/cm3 | 彎曲強度 | 107.84MPa |
彎曲模量 | 2549.02MPa | 成型收縮率 | 1.4% | 加工級別 | 注塑級,脫模級 |
特性級別 | 高流動 |
|
產(chǎn)品簡述
斷裂伸長率 | 200% | 密度 | 1.14g/cm3 | 彎曲強度 | 107.84MPa |
彎曲模量 | 2549.02MPa | 成型收縮率 | 1.4% | 加工級別 | 注塑級,脫模級 |
特性級別 | 高流動 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
機械性能 | 彎曲彈性率 | 23° | ASTM D-790 | 7500 | kgf/cm2 |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 55 | ||
剪切強度 | 23° | ASTM D-732 | 600 | kgf/cm2 | |
彎曲強度 | -30° | ASTM D-790 | 1600 | kgf/cm2 | |
彎曲強度 | 80° | ASTM D-790 | 250 | kgf/cm2 | |
彎曲彈性率 | 80° | ASTM D-790 | 7000 | kgf/cm2 | |
屈服下的伸張強度 | 80° | ASTM D-638 | 320 | kgf/cm2 | |
屈服下的伸張強度 | -30° | ASTM D-638 | 870 | kgf/cm2 | |
1%變形下的壓縮強度23 | ASTM D-695 | 200 | kgf/cm2 | ||
屈服下的伸張強度 | 23° | ASTM D-638 | 400 | kgf/cm2 | |
抗沖擊強度 | 23° | ASTM D-256 | 5.0 | kgf.cm/cm | |
彎曲強度 | 80° | ASTM D-790 | 400 | kgf/cm2 | |
彎曲強度 | 23° | ASTM D-790 | 400 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 120 | ||
彎曲彈性率 | -30° | ASTM D-790 | 34000 | kgf/cm2 | |
抗沖擊強度 | -30° | ASTM D-256 | 3.0 | kgf.cm/cm | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 85 | ||
屈服下的延伸率 | 23° | ASTM D-638 | 8 | % | |
彎曲強度 | -30° | ASTM D-790 | 1350 | kgf/cm2 | |
抗沖擊強度 | 23° | ASTM D-256 | 45 | kgf.cm/cm | |
斷裂下的伸張強度 | 23° | ASTM D-638 | 650 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 85 | ||
屈服下的伸張強度 | -30° | ASTM D-638 | 1100 | kgf/cm2 | |
彎曲彈性率 | 80° | ASTM D-790 | 4000 | kgf/cm2 | |
1%變形下的壓縮強度23 | ASTM D-695 | 100 | kgf/cm2 | ||
彎曲強度 | 23° | ASTM D-790 | 1100 | kgf/cm2 | |
剪切強度 | 23° | ASTM D-732 | 650 | kgf/cm2 | |
屈服下的伸張強度 | 23° | ASTM D-638 | 750 | kgf/cm2 | |
彎曲彈性率 | -30° | ASTM D-790 | 36000 | kgf/cm2 | |
TABER磨耗率 | ASTM D-1044 | 7 | mg | ||
彎曲彈性率 | 23° | ASTM D-790 | 26000 | kgf/cm2 | |
斷裂下的延伸率 | 23° | ASTM D-638 | >200 | % | |
斷裂下的延伸率 | 23° | ASTM D-638 | 100 | % | |
屈服下的伸張強度 | 80° | ASTM D-638 | 180 | kgf/cm2 | |
電氣性能 | 介電常數(shù) | 60HZ | ASTM D-150 | 9.0 | |
介電常數(shù) | 106HZ | ASTM D-150 | 4.5 | ||
介電損耗 | 106HZ | ASTM D-150 | 0.12 | ||
介電常數(shù) | 106HZ | ASTM D-150 | 3.5 | ||
體積電阻率 | ASTM D-257 | 1012 | Ω.cm | ||
介電損耗 | 60HZ | ASTM D-150 | 0.10 | ||
體積電阻率 | ASTM D-257 | 1015 | Ω.cm | ||
抗電弧強度 | ASTM D-495 | 136 | S | ||
絕緣耐力 | ASTM D-149 | 20 | KV/mm | ||
介電損耗 | 103HZ | ASTM D-150 | 0.10 | ||
介電損耗 | 103HZ | ASTM D-150 | 0.02 | ||
介電損耗 | 60HZ | ASTM D-150 | 0.01 | ||
介電常數(shù) | 103HZ | ASTM D-150 | 8.0 | ||
IEC電路 | UL-746 | 600+ | V | ||
介電損耗 | 106HZ | ASTM D-150 | 0.02 | ||
介電常數(shù) | 60HZ | ASTM D-150 | 3.9 | ||
介電常數(shù) | 103HZ | ASTM D-150 | 3.8 | ||
熱性能 | 殘性熱膨脹系數(shù) | ASTM D-696 | 8 | X的10-5cm/cm/°C | |
熔點 | DSC | 215-225 | °C | ||
熱變形溫度 | 4.6kgf/cm2 | ASTM D-648 | 175 | °C | |
熱變形溫度 | 18.6kgf/cm2 | ASTM D-648 | 75 | °C | |
其它性能 | 吸水率 | ASTM D-570 | 10.7 | % | |
成型收縮率 | UBEmethod | 1.4 | % | ||
成型收縮率 | UBEmethod | 1.5 | % | ||
吸水率 | ASTM D-570 | 1.8 | % | ||
燃燒率 | UL-94 | V-2 | |||
比重 | ASTM D-792 | 1.14 |