斷裂伸長率 | 750% | 拉伸強(qiáng)度 | 26MPa | 密度 | 0.92g/cm3 |
熔體流動速率 | 4g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
脆化溫度 | -70℃ |
|
產(chǎn)品簡述
斷裂伸長率 | 750% | 拉伸強(qiáng)度 | 26MPa | 密度 | 0.92g/cm3 |
熔體流動速率 | 4g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
脆化溫度 | -70℃ |
詳細(xì)數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.920 | g/cm3 | ||
熔體流動速率 | ASTM D-1238 | 4.00 | g/10min | |||
物理性能 | 霧度 | ASTM D-1003 | 0.6 | % | ||
薄膜厚度 | HYUNDAI | 25 | um | |||
光澤度 | ASTM D-2457 | 94 | ||||
機(jī)械性能 | 撕裂強(qiáng)度 | MD | TEAR LENGTH 21.5mm | ASTM D-1992 | 60 | % |
TD | TEAR LENGTH 21.5mm | ASTM D-1992 | 210 | % | ||
落球沖擊強(qiáng)度 | ASTM D-1709 | 100 | g | |||
撕裂伸長率 | MD | ASTM D-882 | 650 | % | ||
TD | ASTM D-882 | 750 | % | |||
撕裂拉伸強(qiáng)度 | MD | ASTM D-882 | 350 | kg/cm2 | ||
TD | ASTM D-882 | 270 | kg/cm2 | |||
熱性能 | 低溫脆點 | ASTM D-746 | <-70 | ℃ |