斷裂伸長率 | 800% | 拉伸強(qiáng)度 | 39MPa | 密度 | 0.92g/cm3 |
熔體流動速率 | 2g/10min | 用途級別 | 薄膜級,食品級 | 規(guī)格級別 | 薄膜 |
脆化溫度 | -70℃ | 特性級別 | 透明級 |
|
產(chǎn)品簡述
斷裂伸長率 | 800% | 拉伸強(qiáng)度 | 39MPa | 密度 | 0.92g/cm3 |
熔體流動速率 | 2g/10min | 用途級別 | 薄膜級,食品級 | 規(guī)格級別 | 薄膜 |
脆化溫度 | -70℃ | 特性級別 | 透明級 |
詳細(xì)數(shù)據(jù)
訂購指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.920 | g/cm3 | ||
熔體流動速率 | ASTM D-1238 | 2.00 | g/10min | |||
物理性能 | 光澤度 | 45℃ | ASTM D-2457 | 92 | ||
霧度 | ASTM D-1003 | 1.0 | % | |||
薄膜厚度 | HYUNDAI | 25 | um | |||
機(jī)械性能 | 撕裂伸長率 | MD | ASTM D-882 | 700 | % | |
TD | ASTM D-882 | 800 | % | |||
撕裂強(qiáng)度 | MD | TEAR LENGTH 21.5mm | ASTM D-1992 | 70 | % | |
TD | TEAR LENGTH 21.5mm | ASTM D-1992 | 210 | % | ||
撕裂拉伸強(qiáng)度 | MD | ASTM D-882 | 450 | kg/cm2 | ||
TD | ASTM D-882 | 400 | kg/cm2 | |||
落球沖擊強(qiáng)度 | ASTM D-1709 | 130 | g | |||
熱性能 | 低溫脆點(diǎn) | ASTM D-746 | <-70 | ℃ |