斷裂伸長(zhǎng)率 | 1646% | 拉伸強(qiáng)度 | 29MPa | 密度 | 0.918g/cm3 |
熔體流動(dòng)速率 | 2g/10min | 規(guī)格級(jí)別 | 薄膜 | 缺口沖擊強(qiáng)度 | 89 |
|
產(chǎn)品簡(jiǎn)述
斷裂伸長(zhǎng)率 | 1646% | 拉伸強(qiáng)度 | 29MPa | 密度 | 0.918g/cm3 |
熔體流動(dòng)速率 | 2g/10min | 規(guī)格級(jí)別 | 薄膜 | 缺口沖擊強(qiáng)度 | 89 |
詳細(xì)數(shù)據(jù)
訂購(gòu)指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 |
密度 | ASTM D-1505 | 0.918 | g/cm3 | |
熔體流動(dòng)速率 | 190℃/2.160kg | ASTM D-1238 | 2.0 | g/10min |
混濁度 | ASTM D-1003 | 45.2 | % | |
光澤度 | 45℃ | ASTM D-2457 | 3.2 | % |
極限強(qiáng)度(MD) | ASTM D-882 | 36 | MPa | |
極限強(qiáng)度(TD) | ASTM D-882 | 29 | MPa | |
1%割線模量(MD) | ASTM D-882 | 150 | MPa | |
1%割線模量(TD) | ASTM D-882 | 176 | MPa | |
斷裂伸長(zhǎng)率(MD) | ASTM D-882 | 1401 | % | |
斷裂伸長(zhǎng)率(TD) | ASTM D-882 | 1646 | % | |
Elmendorf撕裂強(qiáng)度(MD) | ASTM D-1922 | 44 | kgF/cm | |
Elmendorf撕裂強(qiáng)度(TD) | ASTM D-1922 | 133 | kgF/cm | |
最小厚度(p/s) | 30 | m | ||
Dart Drop Impact | ASTM D-1709 | 89 | gf/50%f | |
Coeficient of Friction (COF)- Kinetic | ASTM D-1894 | 0.17 |