斷裂伸長率 | 830% | 拉伸強度 | 33MPa | 密度 | 0.92g/cm3 |
熔體流動速率 | 2g/10min |
|
產(chǎn)品簡述
斷裂伸長率 | 830% | 拉伸強度 | 33MPa | 密度 | 0.92g/cm3 |
熔體流動速率 | 2g/10min |
詳細(xì)數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.920 | g/cm3 | ||
熔體流動速率 | ASTM D-1238 | 2.0 | g/10min | |||
物理性能 | 薄膜厚度 | ASTM D-374 | 30 | μm | ||
機械性能 | 斷裂伸長率 | MD | ASTM D-882 | 800 | % | |
TD | ASTM D-882 | 830 | % | |||
拉伸模量 | MD | ASTM D-882 | 2200 | kg/cm2 | ||
TD | ASTM D-882 | 2700 | kg/cm2 | |||
沖擊強度 | ASTM D-1709 | 115 | g | |||
斷裂拉伸強度 | MD | ASTM D-882 | 370 | kg/cm2 | ||
TD | ASTM D-882 | 340 | kg/cm2 | |||
埃門多夫撕裂強度 | MD | ASTM D-1922 | 4 | g/μm | ||
TD | ASTM D-1922 | 7 | g/μm | |||
拉伸屈服強度 | MD | ASTM D-882 | 112 | kg/cm2 | ||
TD | ASTM D-882 | 112 | kg/cm2 | |||
其它性能 | 霧度 | ASTM D-1003 | 2 | % |