斷裂伸長率 | 820% | 拉伸強(qiáng)度 | 41MPa | 密度 | 0.919g/cm3 |
熔體流動(dòng)速率 | 1g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強(qiáng)度 | 11.5 | 加工級別 | 吹塑級 |
|
產(chǎn)品簡述
斷裂伸長率 | 820% | 拉伸強(qiáng)度 | 41MPa | 密度 | 0.919g/cm3 |
熔體流動(dòng)速率 | 1g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強(qiáng)度 | 11.5 | 加工級別 | 吹塑級 |
詳細(xì)數(shù)據(jù)
訂購指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.919 | g/cm3 | ||
熔體流動(dòng)速率 | ASTM D-1238 | 1.0 | g/10min | |||
機(jī)械性能 | 埃爾門多夫撕裂強(qiáng)度 | MD | ASTM D-1922 | 10 | g/μm | |
TD | ASTM D-1922 | 17 | g/μm | |||
伸長率 | MD | ASTM D-882 | 730 | % | ||
TD | ASTM D-882 | 820 | % | |||
拉伸強(qiáng)度(斷裂點(diǎn)) | MD | ASTM D-882 | 500 | kg/cm2 | ||
TD | ASTM D-882 | 420 | kg/cm2 | |||
拉伸強(qiáng)度(屈服點(diǎn)) | MD | ASTM D-882 | 120 | kg/cm2 | ||
TD | ASTM D-882 | 110 | kg/cm2 | |||
抗沖擊強(qiáng)度(Spencer) | ASTM D-3420 | 11.5 | kg.cm | |||
其它性能 | 霧度 | ASTM D-1003 | 12 | % | ||
薄膜厚度 | ASTM D-746 | 50 | μm | |||
添加劑 | SK Method | S,A/B |