斷裂伸長率 | 700% | 拉伸強度 | 34MPa | 密度 | 0.923g/cm3 |
熔體流動速率 | 1.1g/10min | 維卡軟化點 | 106℃ | 用途級別 | 薄膜級 |
|
產品簡述
斷裂伸長率 | 700% | 拉伸強度 | 34MPa | 密度 | 0.923g/cm3 |
熔體流動速率 | 1.1g/10min | 維卡軟化點 | 106℃ | 用途級別 | 薄膜級 |
詳細數(shù)據
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據 | 數(shù)據單位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.923 | g/cc | ||
熔體流動速率 | ASTM D-1238 | 1.1 | g/10min | |||
機械性能 | 斷裂伸長率 | 縱向 | ASTM D-882 | 550 | % | |
橫向 | ASTM D-882 | 700 | % | |||
下降沖擊強度 | ASTM D-1709 | 140 | g | |||
斷裂抗張強度 | 縱向 | ASTM D-882 | 420 | Kg/cm2 | ||
橫向 | ASTM D-882 | 355 | Kg/cm2 | |||
斷裂伸長率 | ASTM D-638 | 900 | % | |||
抗張抗熱強度 | 縱向 | ASTM D-1004 | 110 | Kg/cm | ||
橫向 | ASTM D-1004 | 100 | Kg/cm | |||
斷裂抗張強度 | ASTM D-638 | 220 | kg/cm2 | |||
熱性能 | 熔點 | ASTM D-2117 | 126 | ℃ | ||
維卡軟化點 | ASTM D-1525 | 106 | ℃ | |||
其它性能 | 混濁度 | ASTM D-1009 | 10 | % | ||
光澤度 | 45℃ | ASTM D-2457 | 75 | % | ||
厚度 | HCC | 0.03 | ㎜ |