斷裂伸長率 | 550% | 拉伸強度 | 19MPa | 密度 | 0.921g/cm3 |
熔體流動速率 | 1.5g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 170 |
|
產(chǎn)品簡述
斷裂伸長率 | 550% | 拉伸強度 | 19MPa | 密度 | 0.921g/cm3 |
熔體流動速率 | 1.5g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 170 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.921 | g/cm3 | ||
熔體流動速率 | ASTM D-1238 | 1.5 | g/10min | |||
物理性能 | 試根厚度 | DICM | 50 | μM | ||
模糊度 | ASTM D-1709 | 8 | % | |||
機械性能 | ELMENDORF拉力強度 | MD | ASTM D-1922 | 450 | g | |
TD | ASTM D-1922 | 380 | g | |||
破斷點伸度 | MD | ASTM D-882 | 430 | % | ||
TD | ASTM D-882 | 550 | % | |||
破斷點抗張強度 | MD | ASTM D-882 | 220 | Kg/cm2 | ||
TD | ASTM D-882 | 200 | Kg/cm2 | |||
拉力強度 | MD | ASTM D-1922 | 95 | g | ||
TD | ASTM D-1922 | 90 | g | |||
落球沖擊強度 | ASTM D-882 | 170 | Kg/cm2 |