斷裂伸長率 | 440% | 拉伸強度 | 15MPa | 密度 | 0.923g/cm3 |
熔體流動速率 | 4g/10min | 維卡軟化點 | 93℃ | 用途級別 | 薄膜級 |
規(guī)格級別 | 薄膜 | 加工級別 | 吹塑級 | 特性級別 | 高強度 |
|
產(chǎn)品簡述
斷裂伸長率 | 440% | 拉伸強度 | 15MPa | 密度 | 0.923g/cm3 |
熔體流動速率 | 4g/10min | 維卡軟化點 | 93℃ | 用途級別 | 薄膜級 |
規(guī)格級別 | 薄膜 | 加工級別 | 吹塑級 | 特性級別 | 高強度 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | ASTM D-1505 | 0.923 | g/cm3 | ||
熔體流動速率 | ASTM D-1238 | 4 | g/10min | |||
物理性能 | 光澤 | 60度 | ASTM D-2457 | 10 | ||
光霧 | ASTM D-1003 | 6 | % | |||
機械性能 | 斷裂伸長率 | MD | ASTM D-882 | 250 | % | |
TD | ASTM D-882 | 440 | % | |||
埃爾門多夫撕裂強度 | MD | ASTM D-1938 | 9.5 | CN/mm | ||
TD | ASTM D-1938 | 4 | CN/mm | |||
斷裂拉伸強度 | MD | ASTM D-882 | 19 | MPa | ||
TD | ASTM D-882 | 15 | MPa | |||
屈服拉伸強度 | MD | ASTM D-882 | 12-Dec | MPa | ||
TD | ASTM D-882 | 12-Dec | MPa | |||
1%割線模量 | MD | ASTM D-882 | 220 | MPa | ||
TD | ASTM D-882 | 270 | MPa | |||
落錘沖擊 | ASTM D-1709 | 2.5 | CN/mm | |||
熱性能 | 維卡軟化點 | ASTM D-1525 | 93 | ℃ |