斷裂伸長率 | 420% | 拉伸強度 | 10MPa | 密度 | 0.918g/cm3 |
熔體流動速率 | 6g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 110 |
|
產(chǎn)品簡述
斷裂伸長率 | 420% | 拉伸強度 | 10MPa | 密度 | 0.918g/cm3 |
熔體流動速率 | 6g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
缺口沖擊強度 | 110 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 密度 | 23°C | ASTM D-1505 | 0.918 | g/cm3 | |
熔體流動速率 | ASTM D-1238 | 6.0 | g/10min | |||
機械性能 | 跌落沖擊強度 | ASTM D-1709 | 110 | g | ||
抗張強度 | ASTM D-638 | 110 | Kg/cm2 | |||
抗撕裂張度 | MD | ASTM D-1922 | 250 | g | ||
TD | ASTM D-1922 | 300 | g | |||
屈服點張力 | ASTM D-638 | 90 | Kg/cm2 | |||
破裂點張力 | MD | ASTM D-882 | 180 | kg/cm2 | ||
TD | ASTM D-882 | 160 | kg/cm2 | |||
斷裂伸長率 | ASTM D-638 | 420 | % | |||
斷裂點伸張率 | MD | ASTM D-882 | 380 | % | ||
TD | ASTM D-882 | 530 | % | |||
熱性能 | 維卡軟化點 | ASTM D-1525 | 88 | °C | ||
低溫脆化溫度 | ASTM D-746 | <-76 | °C |