斷裂伸長率 | 715% | 拉伸強度 | 19MPa | 密度 | 0.923g/cm3 |
熔體流動速率 | 0.32g/10min | 維卡軟化點 | 99℃ | 用途級別 | 薄膜級 |
規(guī)格級別 | 薄膜 |
|
產(chǎn)品簡述
斷裂伸長率 | 715% | 拉伸強度 | 19MPa | 密度 | 0.923g/cm3 |
熔體流動速率 | 0.32g/10min | 維卡軟化點 | 99℃ | 用途級別 | 薄膜級 |
規(guī)格級別 | 薄膜 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 熔體流動速率 | 190℃/2.16kg | ASTM D-1238 | 0.32 | g/10min | |
密度 | ASTM D-1505 | 0.923 | g/cm3 | |||
機械性能 | 斷裂拉伸強度 | ASTM D-638 | 19 | MPa | ||
斷裂伸長率 | ASTM D-638 | 715 | % | |||
斷裂拉伸強度 | MD | ASTM D-882 | 37 | MPa | ||
TD | ASTM D-882 | 28 | MPa | |||
斷裂伸長率 | MD | ASTM D-882 | 392 | % | ||
TD | ASTM D-882 | 1037 | % | |||
沖擊強度 | ASTM D-1709 | 99 | gf/50%F | |||
埃爾曼多夫撕裂強度 | ASTM D-1922 | 36 | kgf/cm | |||
熱性能 | 維卡軟化點 | ASTM D-1525 | 99 | ℃ | ||
最初溫度 | Braskem Method | 96 | ℃ | |||
光學性能 | 霧度 | ASTM D-1003 | 13.6 | % | ||
光澤度 | ASTM D-2457 | 7.2 | % |