拉伸強度 | 29MPa | 密度 | 1.16g/cm3 | 熔體流動速率 | 5g/10min |
規(guī)格級別 | 注塑 | 缺口沖擊強度 | 11 | 成型收縮率 | 0.6% |
加工級別 | 注塑級 |
|
產(chǎn)品簡述
拉伸強度 | 29MPa | 密度 | 1.16g/cm3 | 熔體流動速率 | 5g/10min |
規(guī)格級別 | 注塑 | 缺口沖擊強度 | 11 | 成型收縮率 | 0.6% |
加工級別 | 注塑級 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 | 熔體流動速率 | 200℃/5Kg | ASTM D-1238 | 5 | g/10min |
成型收縮率 | ASTM D-955 | 0.4~0.8 | % | ||
比重 | ASTM D-792 | 1.16 | |||
機械性能 | 延伸率 | ASTM D- 638 | 40 | % | |
彎曲彈性率 | ASTM D- 790 | 500 | Kg/cm2 | ||
洛氏硬度 | R-Scale | ASTM D-785 | 88 | ||
撓曲模量 | ASTM D-790 | 20.000 | Kg/cm2 | ||
沖擊強度 | Notched1/8" | ASTM D-256 | 11 | Kg/cm/cm | |
沖擊強度 | Notched1/4" | ASTM D-256 | 8 | Kg/cm/cm | |
抗張強度 | ASTM D- 638 | 300 | Kg/cm2 | ||
電氣性能 | CTI | UL 746A | 2 | PLC | |
HWI | UL 746A | 3 | PLC | ||
抗弧光 | ASTM D-495 | 6 | PLC | ||
HAI | UL 746A | 0 | PLC | ||
HVTR | UL 746A | 1 | PLC | ||
熱性能 | 維卡軟化點 | 1.000g | ASTM D-1525 | 98 | ℃ |
熱變形溫度 | Unannealed18.5g/cm2,1/4" | ASTM D-648 | 78 | ℃ | |
燃燒率 | 1/8" | UL 94 | V-O | ||
燃燒率 | 1/16" | IEC 707 | FVO | mm/min | |
燃燒率 | 1/16" | UL 94 | V-O |