斷裂伸長率 | 660% | 拉伸強(qiáng)度 | 23MPa | 密度 | 0.938g/cm3 |
熔體流動速率 | 0.2g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
脆化溫度 | -75℃ |
|
產(chǎn)品簡述
斷裂伸長率 | 660% | 拉伸強(qiáng)度 | 23MPa | 密度 | 0.938g/cm3 |
熔體流動速率 | 0.2g/10min | 用途級別 | 薄膜級 | 規(guī)格級別 | 薄膜 |
脆化溫度 | -75℃ |
詳細(xì)數(shù)據(jù)
訂購指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 熔體流動速率 | MI | 190℃/2.16kg | ASTM D-1238 | 0.2 | g/10min |
HLMI | 190℃/21.6kg | ASTM D-1238 | 15 | g/10min | ||
密度 | ASTM D-1505 | 0.938 | g/cm3 | |||
機(jī)械性能 | 埃爾門多夫撕裂強(qiáng)度 | MD | ASTM D-1922 | 30 | g | |
TD | ASTM D-1922 | 350 | g | |||
斷裂伸長率 | MD | 50mm/min | ASTM D-882 | 500 | % | |
TD | 50mm/min | ASTM D-882 | 660 | % | ||
抗沖擊強(qiáng)度(Spencer) | ASTM D-3420 | 0.35 | J | |||
落錘沖擊 | 66cm | ASTM D-1709 | 165 | g | ||
屈服拉伸強(qiáng)度 | MD | 50mm/min | ASTM D-882 | 21 | MPa | |
TD | 50mm/min | ASTM D-882 | 23 | MPa | ||
正切彎曲模量 | ASTM D-790 | 760 | MPa | |||
熱性能 | 脆化溫度 | ASTM D-746 | <-75 | ℃ |