斷裂伸長率 | 5% | 拉伸強(qiáng)度 | 40MPa | 密度 | 0.965g/cm3 |
熔體流動速率 | 2.5g/10min | 用途級別 | 薄膜級,食品級 | 規(guī)格級別 | 薄膜 |
彎曲模量 | 1486MPa | 特性級別 | 高強(qiáng)度 |
|
產(chǎn)品簡述
斷裂伸長率 | 5% | 拉伸強(qiáng)度 | 40MPa | 密度 | 0.965g/cm3 |
熔體流動速率 | 2.5g/10min | 用途級別 | 薄膜級,食品級 | 規(guī)格級別 | 薄膜 |
彎曲模量 | 1486MPa | 特性級別 | 高強(qiáng)度 |
詳細(xì)數(shù)據(jù)
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
基本性能 | 熔體流動速率 | ASTM D-1238 | 2.5 | g/10min | ||
熔體流動速率 | 190℃/21.6kg | ASTM D-1238 | 95 | g/10min | ||
密度 | ??松梨诜? | 0.965 | g/cm3 | |||
機(jī)械性能 | 屈服拉伸強(qiáng)度 | MD | ASTM D-882 | 33 | MPa | |
TD | ASTM D-882 | 21 | MPa | |||
斷裂拉伸強(qiáng)度 | MD | ASTM D-882 | 51 | MPa | ||
TD | ASTM D-882 | 40 | MPa | |||
斷裂伸長率 | MD | ASTM D-882 | 774 | % | ||
TD | ASTM D-882 | 5 | % | |||
切割模量 | MD | 1% | ASTM D-882 | 1020 | MPa | |
TD | 1% | ASTM D-882 | 1486 | MPa | ||
埃爾曼多夫撕裂強(qiáng)度 | MD | ASTM D-1922 | 12 | g | ||
TD | ASTM D-1922 | 513 | g |