斷裂伸長(zhǎng)率 | 600% | 拉伸強(qiáng)度 | 29.8MPa | 熔體流動(dòng)速率 | 0.45g/10min |
維卡軟化點(diǎn) | 80℃ | 脆化溫度 | -76℃ |
|
產(chǎn)品簡(jiǎn)述
斷裂伸長(zhǎng)率 | 600% | 拉伸強(qiáng)度 | 29.8MPa | 熔體流動(dòng)速率 | 0.45g/10min |
維卡軟化點(diǎn) | 80℃ | 脆化溫度 | -76℃ |
詳細(xì)數(shù)據(jù)
訂購(gòu)指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |||||
基本性能 | 熔體流動(dòng)速率 | 190℃/2.16kg | ASTM D-1238 | 0.45 | g/10min | ||||
VA含量 | 13.5 | wt% | |||||||
薄膜厚度 | 38.1 | µm | |||||||
機(jī)械性能 | 1%正割模量 | 38.1µm | ASTM D-882 |
|
MPa | ||||
拉伸屈服強(qiáng)度 | 38.1µm | ASTM D-882 |
|
MPa | |||||
拉伸斷裂強(qiáng)度 | 38.1µm | ASTM D-882 |
|
MPa | |||||
屈服伸長(zhǎng)率 | 38.1µm | ASTM D-882 |
|
% | |||||
斷裂伸長(zhǎng)率 | 38.1µm | ASTM D-882 |
|
% | |||||
埃爾曼多夫撕裂強(qiáng)度 | 38.1µm | ASTM D-1922 |
|
g | |||||
落鏢沖擊 | 38.1µm | ASTM D-4272 | 570 | g | |||||
熱性能 | 脆化溫度 | ASTM D-746 | <-76 | ℃ | |||||
維卡軟化溫度 | ASTM D-1525 | 80 | ℃ | ||||||
熔點(diǎn) | DSC | 94.4 | ℃ | ||||||
其它性能 | 氧氣傳輸速率 | 23℃,38.1µm | ASTM D-3895 | 8900 | cm3/m2/24hr | ||||
水蒸氣傳輸速度 | 38℃,38.1µm | ASTM F-372 | 85 | g/m2/24h | |||||
光學(xué)性能 | 光澤度 | 45°,38.1µm | ASTM D-2457 | 88 | |||||
透明度 | 38.1µm | ASTM D-1746 | 78 | ||||||
霧度 | ASTM D-1003 | 1.5 | % |