用途級別 | 薄膜級 | 特性級別 | 阻燃級,耐高溫 |
|
產品簡述
用途級別 | 薄膜級 | 特性級別 | 阻燃級,耐高溫 |
詳細數(shù)據
訂購指南
性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據 | 數(shù)據單位 | |
物理性能 | 熔流率 | 190°C/2.16 kg | ASTM D1238 | 5.2 |
g/10 min
|
醋酸乙烯含量 | ExxonMobil Method | 14.9 |
wt%
|
||
機械性能 | 割線模量 |
1% 正割, MD
|
ASTM D882 | 77.1 |
MPa
|
1% 正割, TD
|
ASTM D882 | 81.4 |
MPa
|
||
抗張強度 |
MD: 斷裂
|
ASTM D882 | 29.6 |
MPa
|
|
TD: 斷裂
|
ASTM D882 | 19.4 |
MPa
|
||
伸長率 |
MD: 斷裂
|
ASTM D882 | 320 |
%
|
|
TD: 斷裂 | ASTM D882 | 870 |
%
|
||
落錘沖擊 |
|
ASTM D1709A | 96 |
g
|
|
埃爾曼多夫抗撕強度 | MD | ASTM D1922 | 210 |
g
|
|
TD
|
ASTM D1922 | 220 |
g
|
||
熱性能 | 維卡軟化溫度 | ASTM D1525 | 63.0 |
°C
|