性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 |
熔流率
|
ASTM D1238 | 2.0 |
g/10 min
|
|
醋酸乙烯含量
|
|
18.0 |
wt%
|
||
硬度計(jì)硬度 | 支撐 A | ASTM D2240 | 91 | ||
機(jī)械性能 | 抗張強(qiáng)度 |
MD: 屈服
|
ASTM D882 | 40.0 |
MPa
|
TD: 屈服
|
ASTM D882 | 30.3 |
MPa
|
||
|
MD: 斷裂
|
ASTM D882 | 4.68 |
MPa
|
|
TD: 斷裂
|
ASTM D882 | 4.30 |
MPa
|
||
伸長(zhǎng)率 |
MD: 屈服
|
ASTM D882 | 410 | % | |
TD: 屈服
|
ASTM D882 | 560 | % | ||
MD: 斷裂
|
ASTM D882 | 9.0 | % | ||
TD: 斷裂
|
ASTM D882 | 9.0 | % | ||
落錘沖擊
|
ASTM D1709A | 610 |
g
|
||
熱性能 |
脆化溫度
|
ASTM D746 |
< -76.0
|
℃ | |
維卡軟化溫度
|
ASTM D1525 | 65.0 | ℃ |