拉伸強(qiáng)度 | 78MPa | 密度 | 1.07g/cm3 | 熔體流動速率 | 1.8g/10min |
缺口沖擊強(qiáng)度 | 2 | 成型收縮率 | 0.4% |
|
產(chǎn)品簡述
拉伸強(qiáng)度 | 78MPa | 密度 | 1.07g/cm3 | 熔體流動速率 | 1.8g/10min |
缺口沖擊強(qiáng)度 | 2 | 成型收縮率 | 0.4% |
詳細(xì)數(shù)據(jù)
訂購指南
性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
物理性能 | 流動系數(shù) | 220℃/10kg | ASTM D-1238 | 18 | g/10min |
變縮性 | ASTM D-955 | 0.2~0.6 | % | ||
比重 | ASTM D-792 | 1.07 | |||
流動系數(shù) | 220℃/5kg | ASTM D-1238 | 1.8 | g/10min | |
機(jī)械性能 | 彎曲模數(shù) | ASTM D-790 | 39,000 | kg/cm2 | |
拉伸強(qiáng)度 | ASTM D-638 | 800 | kg/cm2 | ||
IZOD沖擊強(qiáng)度 | Notched1/8" | ASTM D-256 | 2.0 | kg·cm/cm | |
彎曲強(qiáng)度 | ASTM D-790 | 1300 | kg/cm2 | ||
洛氏硬度 | R-Scale | ASTM D-785 | 122 | ||
IZOD沖擊強(qiáng)度 | Notched1/4" | ASTM D-256 | 1.5 | kg·cm/cm | |
伸長率 | ASTM D-638 | 6 | % | ||
熱性能 | 燃燒性 | 1/16" | IEC707 | - | mm/min |
燃燒性 | 1/8" | UL-94 | HB | ||
燃燒性 | 1/16" | UL-94 | HB | ||
燃燒性 | 1/12" | UL-94 | - | ||
燃燒性 | 1/8" | IEC707 | FH3-27 | mm/min | |
維卡軟化點(diǎn) | 1,000g | ASTM D-1525 | 110 | ℃ | |
熱變形溫度 | Unannealed 18.5kg/cm21/2" | ASTM D-648 | 90 | ℃ |