加工級別 | 注塑級 | 特性級別 | 高流動,高抗沖 |
|
產(chǎn)品簡述
加工級別 | 注塑級 | 特性級別 | 高流動,高抗沖 |
詳細數(shù)據(jù)
訂購指南
性能項目 | 測試條件 | 測試方法 | 數(shù)值/描述 | 單位 | |
機械性能 | 拉伸強度(引張強度) | ASTM D638/ISO 527 | 40 | kg/cm²(MPa)[Lb/in2] | |
斷裂伸長率 | ASTM D638/ISO 527 | 2.7 | % | ||
拉伸模量 | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in2] | |||
拉伸屈服伸長率(延伸率) | ASTM D638/ISO 527 | % | |||
拉伸斷裂伸長率(延伸率) | ASTM D638/ISO 527 | % | |||
彎曲模量(彎曲彈性率) | ASTM D790/ISO 178 | 58 | kg/cm²(MPa)[Lb/in2] | ||
彎曲強度 | ASTM D790/ISO 178 | kg/cm²(MPa)[Lb/in2] | |||
洛氏硬度 | ASTM D785 | ||||
IZOD 缺口沖擊強度 | 1/4" 23℃ | ASTM D256/ISO 179 | 31 | kg·cm/cm(J/M)ft·lb/in | |
1/4" -30℃ | ASTM D256/ISO 179 | 11 | kg·cm/cm(J/M)ft·lb/in | ||
1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
Charpy沖擊強度 | 23℃ (缺口) | ASTM D256/ISO 179 | 30 | kg·cm/cm(J/M)ft·lb/in | |
-30℃(缺口) | ASTM D256/ISO 179 | 11 | kg·cm/cm(J/M)ft·lb/in | ||
23℃(無缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
-30℃(無缺口) | ASTM D256/ISO 179 | 160 | kg·cm/cm(J/M)ft·lb/in | ||
物性性能 | 比重(密度) | ASTM D792/ISO 1183 | 1.02 | ||
成型收縮率 | ASTM D955 | 0.4-0.7 | % | ||
熔融指數(shù)(流動系數(shù)) | 200℃/5kg | ASTM D1238/ISO 1133 | g/10min | ||
220℃/10kg | ASTM D1238/ISO 1133 | g/10min | |||
吸水率 23℃/24H | ASTM D570/ISO 62 | 1.03 | % | ||
熱性能 | 熱變形溫度 | 退火 | ASTM D648/ISO 75 | 97 | ℃(℉) |
未退火 | ASTM D648/ISO 75 | 102 | ℃(℉) | ||
維卡軟化點 | ASTM D1525/ISO R306 | 104 | ℃(℉) | ||
熔點 | - | ℃(℉) | |||
燃燒性(率) | UL94 | ||||
線性膨脹系數(shù) | ASTM D696/ISO 11359 | 0.8-1.1 | mm/mm.℃ | ||
加工條件 | 干燥條件 | ||||
加工溫度 | 射嘴 | ℃ | |||
料筒前段 | ℃ | ||||
料筒中段 | ℃ | ||||
料筒后段 | ℃ | ||||
熔體溫度 | ℃ | ||||
模具溫度 | ℃ | ||||
壓力 | 注塑壓力 | Mpa | |||
保壓壓力 | Mpa | ||||
背壓 | Mpa | ||||
螺桿轉(zhuǎn)速 | rpm | ||||
其他 | 備注 | ||||
顏色 | |||||
特性 | |||||
用途 |